PRODUCTS
THASSOS
Petrographic description
95% Do, 4% Cc, 1% Kf
End use
Internal and External
Abrasion resistance
21,7 mm
Water absorption
0,14 %
PIRGON
Petrographic description
97% Do, 3% Cc
End use
Internal and External
Abrasion resistance
0,58%
Water absorption
0,37 %
VOLAKAS
Apparent density
2840 Kg/m3
Flexural strength
6,3 MPa
Abrasion resistance
25263 mm3
Water absorption
0,2 %
Frost resistance
5,8 MPa
KAVALAS
Apparent density
2700 Kg/cm3
Frost resistance
10,7 MPa
Abrasion resistance
30679 mm3
Water absorption
0,10 % wt
POLARIS
Apparent specific weight
2852 Kg/m3
Absorption coefficient
0,17 % wt
Compressive strength
1224 Kg/cm2
Modulus of rupture
106 Kg/cm2
Abrasion resistance
2,84 mm
DRACO
Petrographic description
61,48% Cc, 7,69% Do, 23,10% Qz, 12,57% Albite
End use
Internal and External
Abrasion resistance
20,2 mm
Water absorption
0,43 %
DAMASTAS
Apparent density
2657,3 Kg/cm
Compressive strength
163,06 N/mm2
Frost resistance
-9,9%
Water absorption
1,5%
Flexural strength
7,94,19 N/mm2
LIVADIAS
Apparent density
2700 Kg/m3
Abrasion resistance
16939 mm3
Frost resistance
12,7 MPa
Water absorption
0,2%
ALIVERI
Petrographic description
93% Cc, 4% Do, 2% Qz, 1% Clr
End use
Internal and External
Abrasion resistance
23,9 mm
Water absorption
0,2 %
PERLA
Apparent density
2610 Kg/m3
End use
Internal and External
Compressive strength
92 N/mm2
Flexural strength
13,1 N/mm2
Water absorption
1,1 %
VRATSA
Slip resistance
Dry 72 SRV – Wet 67 SRV
Water absorption
3,9-4,8 % wt
Frost resistance
0,50 -0,65 MPa
TRIESTA
Apparent specific weight
2648 Kg/m3
Absorption coefficient
0,40 % wt
Compressive strength
22900 min 7500 psi
Modulus of rupture
22000 min 1000 psi
Abrasion resistance
38,7 min Ha 10
SAMAHA
Apparent density
2640 Kg/cm3
Absorption by weight
0.90%
Compressive strength
65,7 MPa
Flexural strength
10,5 MPa
Abrasion resistance-Hardness
23
SUNNY
Apparent specific weight
2628 Kg/m3
Absorption coefficient
0,35 % wt
Compressive strength
85 MPa
Modulus of rupture
13,5 MPa
Abrasion resistance
25
VERDE RAJASTAN
Density
2,65 gr/cm3
Water absorption
0,06 % wt
Compressive strength
Dry 299 n/mm2 – Wet 159 n/mm2
Modulus of rupture
Dry 33 n/mm2 – Wet 28 n/mm2
Abrasion resistance
1 mm